We report on the use of open-air blade-coating as a scalable method for producing metal halide perovskite films with >10× fracture energy for durability and mechanical stability through the addition of corn starch polymer additives. This results in a manufacturable and robust perovskite that has tunable thicknesses exceeding 10 µm, among the highest reported values for solution-processed polycrystalline films. We find that an increasing amount of starch causes more uniform carbon distribution within the perovskite thickness as quantified by cross-sectional elemental composition measurements. Further, the incorporation of starch introduces beneficial compressive film stresses. Importantly, the optoelectronic behavior is not compromised, as the photoluminescence spectrum becomes more homogenous with the addition of corn starch up to 20% by weight. 

We report on the use of 2D Ruddlesden–Popper (RP) perovskites as optoelectronic materials in building-integrated applications, addressing the challenge of balancing transparency, photoluminescence, and stability. With the addition of polyvinylpyrrolidone (PVP), the 2D RP films exhibit superior transparency compared to their 3D counterparts with an average visible transmittance (AVT) greater than 50% and photoluminescence stability under continuous illumination and 85 °C heat for up to 100 h as bare, unencapsulated films. Structural investigations show a stress relaxation in the 3D perovskite films after degradation from thermal aging that is not observed in the 2D RP films, which retain their phase after thermal and light aging. We also demonstrate ultrasmooth, wide-bandgap 2D Dion–Jacobson (DJ) films with PVP incorporation up to 2.95 eV, an AVT above 70%, and roughnesses of ~2 nm. These findings contribute to the development of next-generation solar materials, paving the way for their integration into built structures.